Slow Hardener (West System)
The West System 206 Slow Hardener is ideal for general bonding and coating applications. It is a low-viscosity epoxy curing agent that can be used when prolonged cure time is required to provide enough working time at high temperatures.
This agent when mixed with 105 resin in the ratio of 5:1 (resin-hardener) gives you a highly strong and moisture resistant solid. This hardener is perfect for general bonding, fabric application and barrier coating.
- Low-viscosity epoxy curing agent
- Can be used when prolonged working and cure time is required
- Cured mixture has amazing bonding and coating properties
Features of West System 206 Slow Hardener
- 5:1 resin-hardener mixture yields a strong and moisture resistant solid
- Suitable for general bonding, fabric application and barrier coating
Specifications
Manf. Part #: 206A
- Size: 0.44 Pint
- Pot life at 72°F (22°C): 20 to 25 minutes
- Cure to a solid state: 10 to 15 hours
- Cure to maximum strength: 1 to 4 days
- Minimum recommended temperature: 60°F (16°C)
Manf. Part #: 206B
- Size: 0.86 Quart
- Pot life at 72°F (22°C): 20 to 25 minutes
- Cure to a solid state: 10 to 15 hours
- Cure to maximum strength: 1 to 4 days
- Minimum recommended temperature: 60°F (16°C)
Hardener | Uses Resin/Hardener | Hardener Temperature Range (F) | Cure Speeds at 72 degrees | ||
---|---|---|---|---|---|
Pot Life: 100g cupful | Working Time: thin film | Cure to Solid: thin film | |||
205 Fast Hardener | General bonding, fabric application and barrier coating | 45-85 degrees | 9-12 min | 60-70 min | 6-8 hours |
206 Slow Hardener | General bonding, fabric application and barrier coating | 60-90 degrees | 20-25 min | 90-110 min | 10-15 hours |
207 Special Clear Hardener | Clear fabric application and clear coating for a natural wood finish | 60-90 degrees | 22-27 min | 110-130 min | 12-18 hours |
209 Extra Slow Hardener | General bonding, fabric application and barrier coating | 65-100 degrees | 40-50 min | 3-4 hours | 20-24 hours |